XL-2356is a solvent-dispersed colloidal graphite that air dries to the touch in
10 minutes, and completely cures in 30 minutes.
XL-2356penetrates and adheres tenaciously to most metallic substrates with minimal surface
pretreatment and preparation. Although this procedure is adequate with
most applications, to achieve maximum corrosion and rust resistance, surfaces
should be thoroughly cleaned and sandblasted prior to application.
an exceptionally stable, rust/corrosion resistant, and tough micro-graphite
coating highly resistive to temperature fluctuations from -60°C to 400°C.
Because of its excellent adhesion to metallic surfaces and dry film consistency,XL-2356reduces
potential environmental problems caused by conventional lubricating greases due
to water wash-off from rain and snow, and product melting from exposure to the
• Thin opaque film
• High lubricity
• Lubrication at temperature extremes
• Excellent adhesion
• Good electrical conductivity
• Excellent rust and corrosion resistance
• Room-temperature curing
• Prevents galling, fretting & seizing
• Long lasting
• Will not plug application equipment
DILUTION: XL-2356is thixotropic in nature and will gel during storage. Preparation involves mild
agitation and dilution (if required) to the consistency required for the
application method chosen.
Can be applied by spray, brush, dip, or roller methods. Always agitate
thoroughly prior to use.
Coating air dries to touch in ten minutes under normal ambient conditions.
Full cure properties develop in approximately thirty minutes depending on
the film thickness.